6063 aluminum t bar

Product name: 6063 aluminum t bar
Material name: 6063
Standard: GB/T 3191-1998
 
Features of 6063 aluminum t bar
 
6063 aluminum bar is a low-alloy Al-Mg-Si series high-plasticity alloy. Has many valuable features:
 
1. Strengthened by heat treatment, high impact toughness, insensitive to defects.
2. It has excellent thermoplasticity and can be extruded at high speed into complex, thin-walled, hollow profiles or forgings with complex structures. The quenching temperature range is wide, and the quenching sensitivity is low. After extrusion and forging demoulding, As long as the temperature is higher than the quenching temperature. It can be quenched by spraying or penetrating water. Thin-walled parts (6<3mm) can also be wind quenched.
3. Excellent welding performance and corrosion resistance, no stress corrosion cracking tendency. Among the heat-treatable aluminum alloys, the Al-Mg-Si series alloy is an alloy with no stress corrosion cracking phenomenon.
4. After processing, the surface is very smooth and easy to anodize and color. The disadvantage is that if it is left at room temperature for a period of time after quenching, the strength will be adversely affected (parking effect).


 
6063 aluminum alloy is a medium-strength heat-treatable and strengthened alloy in the AL-Mg-Si series. Mg and Si are the main alloying elements. The main task of optimizing the chemical composition is to determine the percentage of Mg and Si (mass fraction, the same below) .
 
1.1 The role and influence of Mg Mg and Si form the strengthening phase Mg2Si. The higher the content of Mg, the greater the amount of Mg2Si, the greater the heat treatment strengthening effect, the higher the tensile strength of the profile, and the higher the deformation resistance. If it increases, the plasticity of the alloy decreases, the processing performance deteriorates, and the corrosion resistance deteriorates.
1.2 The role of Si and the influence of the amount of Si should enable all Mg in the alloy to exist in the form of Mg2Si phase to ensure that the role of Mg is fully exerted. As the Si content increases, the grains of the alloy become finer, the fluidity of the metal increases, the casting performance becomes better, the heat treatment strengthening effect increases, the tensile strength of the profile increases, the plasticity decreases, and the corrosion resistance deteriorates.
 
The chemical composition of 6063 aluminum t bar
Aluminum Al: margin
Silicon Si: 0.20～0.60
Copper Cu: 0.10
Magnesium: 0.45～0.9
Zinc Zn: 0.10
Manganese Mn: 0.10
Titanium Ti: 0.10
Chromium Cr: 0.10
Iron Fe: 0.35
Single: 0.05 Total: 0.15
 
6063 aluminum t bar mechanical properties
 
Tensile strength σb (MPa): 130～230
The ultimate tensile strength of 6063 is 124 MPa
 
Tensile yield strength 55.2 MPa
Elongation rate 25.0%
Elasticity coefficient 68.9 GPa
Bending ultimate strength 228 MPa Bearing Yield Strength 103 MPa
Poisson's ratio 0.330
Fatigue strength 62.1 MPa　
The solution temperature is: 520℃
The annealing temperature is: 415℃×(2-3)h, cooling from 415℃ to 260℃ at 28℃/h.
Melting temperature: 615～655℃.
Specific heat capacity: 900
Heat treatment process: excellent workmanship
 
The purpose of 6063 aluminum t bar
 
Building profiles, irrigation pipes, extrusion materials for vehicles, benches, furniture, elevators, fences, etc., as well as decorative components of different colors for aircraft, ships, light industry departments, buildings, etc.

Author: Frank

Chalco Aluminium is specialized in producing and marketing aluminium bar.Our customer service representatives are qualified,knowledgeable aluminum bars experts, Thire industry expertise and professionalism will save you time and money and ensure that you have the best aluminium bars and rods.

6063-t52 aluminum flat bar

6063 aluminum flat bar contains two main alloying elements, namely magnesium and silicon, which have good processability, excellent weldability, extrudability and electroplating, good corrosion resistance, toughness, easy to light, and upper coating ,...

Aluminum billet 6063

Aluminum billet 6063 has excellent processability, excellent weldability and excellent anodizing effect Aluminum bill 6063 material. The main alloy elements are magnesium and silicon. It is a typical extruded alloy with excellent processability, excel...

6063 t6 aluminum bar

6063 t6 aluminum bar rod belongs to the Al-Mg-Si series alloy, with good extrudability, can be used as a shape with complex cross-sectional shape, good corrosion resistance and surface treatment, and a wide range of applications, especially the constructi...

6063 high precision aluminum bar

6063 high precision aluminum bar, The main alloy elements are magnesium and silicon, which have excellent processing performance, excellent weldability, extrudability and electroplating, good corrosion resistance and toughness, easy to polish and color fi...