7075 t7351 round bar

7075 t7351 round bar contains zinc and magnesium. The common aluminum alloy has high strength, but it can't be welded, and its corrosion resistance is quite poor. Many parts manufactured by CNC machining use 7075 t7351 round bar. Zinc is the main alloy element in this series. With a little magnesium alloy, the material can be heated to achieve very high strength. This series of materials are generally added with a small amount of copper, chromium and other alloys. Among them, 7075 t7351 round bar is the best one with high strength, which is suitable for aircraft frames and high-strength accessories



7075 t7351 round bar composition:
Si: 0.40
Fe: 0.50
Cu: 1.2-2.0
Mn: 0.30
Mg: 2.1-2.9
Cr: 0.18-0.28
Zn: 5.1-6.1
Ti: 0.20
Aluminum: allowance
Others: single: 0.05 total: 0.15
Mechanical properties of 7075 t7351 round bar with diameter of 25 mm:
Tensile strength σ b (MPa)：≥560
Elongation stress σ p0.2 (MPa)：≥495
Elongation δ 5 (%)：≥6

Author: Frank

Chalco Aluminium is specialized in producing and marketing aluminium bar.Our customer service representatives are qualified,knowledgeable aluminum bars experts, Thire industry expertise and professionalism will save you time and money and ensure that you have the best aluminium bars and rods.

7075 T651 Aluminium rectangular bar

The main alloying element of 7075 is zinc, and magnesium can also be added to form an alloy with a significant strengthening effect. After heat treatment, the alloy can achieve very high strength. In this series of alloys, 7075-T651 is a very high-quality...

7075 t6 aluminum billet

The 7XXX series aluminum alloy belongs to the Al-Zn-Mg-Cu series super-duralumin. The 7075 t6 aluminum billet is a high-strength deformed aluminum that has been used in the aircraft industry in the late 1940s and is still widely used in the aviation indus...

7075 t6 aluminum billet

...

7075 T6 ASTM B221-08 aluminum alloy bar

7075 aluminum alloy bar is a cold-treated forged alloy bar with high strength, far superior to mild steel. 7075 is one of the strongest alloys commercially available. General corrosion resistance, good mechanical properties and anode reaction. The fine gr...