2A12 t351 T4 aluminum alloy bar rod

2A12 t351 T4 aluminum alloy bar rod belongs to Al Cu my aluminum alloy. Its main characteristics and application range are as follows: it is a kind of high-strength hard aluminum, which can be strengthened by heat treatment. It has medium shape under quenching and hard quenching, good spot welding, and tendency to form intergranular cracks during gas welding. Its machinability is good after quenching and cold hardening, but low after annealing, Because of its poor corrosion resistance, anodizing and painting are often used to improve its corrosion resistance.
2A12 t351 T4 aluminum alloy bar rod is mainly used to make all kinds of high load parts and components (excluding stamping parts and forgings), such as aircraft skeleton parts, skin, partition frame, wing rib, wing beam, rivet and other working parts below 150 ℃.


 

Alloy	Si	Fe	Cu	Mn	Mg	Cr	Zn	Ti	Others		Al
2a12	0.5	0.5	3.8-4.9	0.3-0.9	1.2-1.8	--	0.3	0.15	Every	Total
											remainder

 
Henan Chalco is the supplier of 2a12-t351 T4 aluminum bar. It produces high-quality 2a12-t351 T4 aluminum bar and 2A12 aluminum square bar. It has complete specifications of 2a12-t351 and 2A12-T4 aluminum bar in stock. It provides price information and quotation sheet of 2a12-t351 aluminum bar, and finds high-precision 2a12-t351 material in Henan Chalco.

China 2A12 aluminum round bar rod manufacture

2A12 aluminum alloy rod is a kind of high-strength hard aluminum, which can be heat-treated and strengthened; 2A12 aluminum alloy has good spot weldability, and there is a tendency to form intergranular cracks when using gas welding and argon arc weld...

2A12 H112/T4 aluminum square bar

2A12 H112/T4 aluminum square bar is a kind of high-strength hard aluminum, which can be heat-treated and strengthened; 2A12 aluminum alloy has good spot weld ability, and there is a tendency to form inter granular cracks when using gas welding and argon a...

what is the 2a12 aluminum round bar rod

2a12 aluminum round bar rod 2a12 aluminum round bar rod is a kind of high-strength hard aluminum which can be heat-treated and strengthened. It has medium plasticity in annealing, quenching and hot state. It has good spot welding and good tendency to form...